Cold Drawn 304 Stainless Steel Flat Bar

All Grades Comparison:
ASTM	JIS	GB
304	SUS 304	06Cr19Ni10

Chemical Composition(%)
Steel Grade	C	Si	Mn	P	S	Cr	Ni	N
304	0.08 max	1.00 max	2.0 max	0.045 max	0.030 max	18.0-20.0	8.0-11.0	/
304L	0.03 max	1.00 max	2.0 max	0.045 max	0.030 max	18.0-20.0	8.0-12.0	/
304N	0.08 max	1.00 max	2.0 max	0.045 max	0.030 max	18.0-20.0	8.0-11.0	0.10-0.16

Mechanical Properties
Steel Grade	Delivery Condition	Thickness	Tensile Strength (Mpa)	Yield Strength (Mpa)	Elongation in 2 in. (50 mm)	Reduction of Area
304	Annealed	12.7mm max	620 Mpa min	310 Mpa min	30% min	40% min
304	Annealed	12.7mm min	515 Mpa min	205 Mpa min	30% min	40% min
304L	Annealed	12.7mm max	620 Mpa min	310 Mpa min	30% min	40% min
304L	Annealed	12.7mm min	485 Mpa min	170 Mpa min	30% min	40% min
304N	Annealed	Whole Sizes	550 Mpa min	240 Mpa min	30% min	/
304/304L/304N	Relatively severe cold work	19.5mm – 25.4mm	795 Mpa min	550 Mpa min	15% min	35% min
304/304L/304N	Relatively severe cold work	25.4mm – 31.75mm	690 Mpa min	345 Mpa min	24% min	45% min
304/304L/304N	Strain Hardened	50.8mm max	650 Mpa min	515 Mpa min	25% min	40% min