316 420C 440C 304 stainless steel ball

aterial	Feature	General Applications
AISI 420	Magnetic, Harden-able,  fair corrosion resistance	used for special bearings and valves where  Balls requiring a combine -action of hardness and  corrosion resistance
AISI 440C	Magnetic, highest hardness,  good corrosion resistance	used in bearing nozzles and valves where  lubrication is poor or absent
AISI 304	austentitic, corrosion resistance,  slightly magnetic, however annealing  can makes it non - magnetic	Used in valves and relevant application ,  food products, aerosols, home sprays,  perfumes and medical equipment.
AISI 316	non - magnetic, good corrosion  resistance even when exposed to  marine atmosphere and sulfuric acid.	used in presence of sulphuric, phosphoric  and acetic acids. Mainly used in chemical, paper and textile industries.
AISI 316	Characteristics same as 316 but  with excellent corrosion resistance, Lower carbon content than regular 316.	expecially used in Jewelry,  and Human Implant Applications

CHINA	USA	JAPAN	GERMANY	SWEDEN
GB	AISI	JIS	DIN	SIS
9Cr18Mo	440C	SUS440C	X110CrMo15	3230
1Cr18Ni9	302	SUS302	X12CrNi188	1.43
0Cr19Ni 9	304	SUS304	X5CrNi189	1.4301
0Cr17Ni12Mo2	316	SUS316	X5CrNiMn18	10(1.4401)
3Cr13	420	SUS420J2	X30Cr13	1.4028

Material	C	Si	Mn	P	S	Ni	Cr	Mo
AISI304	0.07 max	1.0 max	2.0 max	0.045 max	0.03 max	8.0-10.5	17.0-19.0
AISI316	0.07 max	1.0 max	2.0 max	0.045 max	0.03 max	10.0-14.0	16.5-18.5	2.00-2.50
AISI420C	0.40-0.50	1.0 max	1.0 max	0.04 max	0.03 max	1.0 max	12.0-14.0
AISI440C	0.95-1.20	1.0 max	1.0 max	0.04 max	0.03 max	0.60 max	16.0-18.0	0.40-0.80