9.5mm bare Aluminium Wire Rod

It is mainly used for drawing the core of wires and cables

The surface of the rod is clean, smooth and seamless.

Coil weight: large coil≤1000kg, small coil: 300--1000kg

Aluminum Rod was produced and provided by consulting and following the American standard ASTM B233 and Germany standard EN17152

1.Producing and providing the products according to Chinese standard GB/T3954-2001, and consulting and following the American standard ASTM B233:1997, and Germany DIN standard EN 17152:1997

  aluminium rod

 

2.The Type,Condition and Range

Type	Condition	Range(mm)
A	o	Φ9-20
A2,A4,A6,A8	H/R

  aluminium rod

 

3.The Mechanics and Electric Function

Type	Tensile Strength (M pa)	Percentage Elongation (%≥)	Resistivity at 20°c (nΩ.m≤)
A	60-80	25	27.55
A2	80-100	12	27.85
A4	95-115	10	28.01
A6	110-130	8	28.01
A8	120-150	6	28.01

 

4.The Component of Material

Name of Element	Si	Fe	Cu	V+Ti+Mn+Cr	Other	Al
Percentage %	≤0.11	0.25	0.01	0.02	0.03	≥ 99.61

  aluminium rod

 

5.Standard specification for Aluminum 1350 Drawing Stock for Electrical Purposes

 

TABLE 1- Tensile Property Limits

Temper	Tensile Strength
	Ks j	M pa
1350-O	8.5-14.0	59-97
1350-H12 and-H22	12.0-17.0	83-117
1350-H14 and-H24	15.0-20.0	103-138
1350-H16 and-H26	17.0-22.0	117-152

 

TABLE 2- Electrical Resistivity Limits

Temper	Resistivity	Equivalent Volume Conductivity,%
	Max.Ω.mm2/m	IACS Min.
1350-O	0.027899	61.8
1350-H12 and-H22	0.028035	61.5
1350-H14 and-H24	0.028080	61.4
1350-H1 aluminium rod 6 and-H26	0.028126	61.3